Fwd: [ATM] Open Question Concerning Pitch Laps

[Bryan Stiles <bryan.stiles@gmail.com>]

I did not scrape or brush the lap. Is there some guideline I should
use to recognize when to do this? Now at the outset I didn't wash the
lap off after use. Eventually the CeO mix built up and I used a soft
brush to remove that and generally clean it up a bit. I should also
mention that when not in use I store the lap in a plastic, sealed
container.

Bryan


---------- Forwarded message ----------
From: Ken Lowther <hermit@outofoptions.org>
Date: Mon, 28 Feb 2005 16:26:54 -0500
Subject: Re: [ATM] Open Question Concerning Pitch Laps
To: atm@atmlist.net



Quoting Bryan Stiles <bryan.stiles@gmail.com>:

> I have experienced a phenomenon on two separate occasions that I would
> appreciate some input on.
>
> This question is a direct result of my prior posts about the inability
> to remedy a central hole in my mirror. I tried all the suggestions
> kindly provided but to no avail...I went back to fine grinding. In a
> nutshell the question is why does my lap quit responding?
>

Have you tried wire brushing or scraping the surface?  Is your lap too
thing?  Is it possible it has become too hard?

Ken

----------------------------------------------------------------
This message was sent using IMP, the Internet Messaging Program.

_______________________________________________
ATM mailing list http://www.atmlist.net/
_______________________________________________
ATM mailing list http://www.atmlist.net/